S-Glass Roving (High Strength Glass Fiber)
CYC S-Glass Roving (HS2, HS4, HS6) is made from magnesium-alumina-silicate glass system. Foreign countries named as R-glass or T-glass. Due to its high tensile strength, high tensile modulus, excellent impact resistance, aging & corrosion resistance properties, S-Glass fiber is designed for high performance composites industries specially, such as military, aerospace, defense, marine & shipbuilding, civil industry, sports and recreation industry worlwide.
PRODUCT FEATURES:
High tensile strength
High tensile modulus
Compatible with Epoxy, Phenolic & Vinly ester resin
Excellent aging & corrosion resistance
S-GLASS FIBER PROPERTIES:
|
Physics Properties
|
HS2 |
HS4 |
HS6 |
| Original Fiber Tensile Strength (MPa) |
≥4100 (590KSI) |
≥4600 (660KSI) |
≥4800 (690KSI) |
| Epoxy Wet Fiber Tensile Strength (MPa) |
3000~3400 (435~490KSI) |
3200~3600 (460~520KSI) |
3600~4000 (520~580KSI) |
| Tensile Modulus (GPa) |
87~91 |
90~94 |
92~96 |
| Elongation at Break (%) |
5.3 |
5.3 |
5.7 |
| Softening Point (℃) |
910 |
940 |
960 |
TYPICAL PRODUCT SPECIFICATIONS:
| Product Code |
Filament Diameter (μm) |
Linear Density (tex) |
Tensile Strength
(MPa)
|
Moisture Content (%) |
Loss On Ignition (%) |
Compatible Resin |
| SCY11-HS2-240 |
11 |
240 |
≥3000 |
≤0.20 |
0.50~1.10 |
EP/VE/PE |
| SCY11-HS4-240 |
11 |
240 |
≥3200 |
≤0.20 |
0.50~1.10 |
| SCY11-HS6-240 |
11 |
240 |
≥3600 |
≤0.20 |
0.50~1.10 |
| SCY11-HS2-660 |
11 |
660 |
≥3000 |
≤0.20 |
0.50~1.10 |
| SCY11-HS4-660 |
11 |
660 |
≥3200 |
≤0.20 |
0.50~1.10 |
| SCY11-HS6-660 |
11 |
660 |
≥3600 |
≤0.20 |
0.50~1.10 |
| SCY17-HS2-2400 |
17 |
2400 |
≥3000 |
≤0.20 |
0.50~1.10 |
Notes: Customized specification is available.
PACKAGING:
CYC S-Glass Roving packed by standard exporting carbon boxes and pallets.
STORAGE:
Unless otherwise specified, CYC S-Glass roving should be stacked in dry and cool place with its original package, do not open the package cause damp.