Alkali Resistant Glassfiber Spray Roving with Standard Zirconia above 14.5% (ZrO2>14.5%)
Alkali Resistant Glassfiber Spray Roving with Standard Zirconia above 14.5% (ZrO2>14.5%) is designed for GRC (Glassfiber Reinforced Cement) or GFRC (Glass Fiber Reinforced Concrete) composites components by spray up process specially. It is designed for optimum processability and widely used in the manufacture of GRC architectural panels and other building elements, civil engineering and infrastructure components.
Example : ARG15-2400L
AR: Alkali Resistant
G: Continuous Glassfiber Roving
15: Filament diameter(um)
2400: Nominal linear weight of roving (tex)
L: Zirconia content above 14.5% (ZrO2>14.5%)
Product Characteristics:
a. Good Choppability
b. Good Integrity
c. Excellent dispersibility and Alkali Resistant Ability
d. Excellent frost-resistant, moisture-resisitant, crack resistance and impermeability
Technical Data:
|
linear weight of roving(tex)
|
Sizing content(%)
|
Moisture(%)
|
Stifness(mm)
|
Breaking strength(N/tex)
|
|
JC/T572-2002
|
JC/T572-2002
|
JC/T572-2002
|
JC/T572-2002
|
JC/T572-2002
|
|
2400±240
|
1.3±0.2
|
≤0.2
|
≥120
|
≥0.25
|
Products Available:
Alkali Resistant Glassfiber Spray Roving with Standard Zirconia content above 14.5% (ZrO2>14.5%) is designed to be unwound internally. They are protected by a shrink-wrap polythene film which should not be removed before using. Each AR Spray roving bobbin marked by a label for identify.
|
Product
|
Packing specification(mm)
|
Characteristics
|
|
Height
(mm)
|
Diameter
(mm)
|
Net Weight
(kg)
|
|
ARG15-2400L
|
290×290×300
|
270
|
280
|
20(±2)
|
Pallet Packaging:
|
Product Code
|
Level
per Pallet
|
Total number
of Bobbins
|
Pallet
|
|
Length
(mm)
|
Width
(mm)
|
Height
(mm)
|
Net Weight
(kg)
|
|
ARG15-2400L
|
|
|
3
|
48
|
1130
|
1130
|
1000
|
1000
|
|
4
|
64
|
1130
|
1130
|
1300
|
1150
|
Shipment:
For sea transportion, a maximum of 20 pallets (by two levels) will be loaded in a 20' foot container,
giving a total net weight approximately 17-20MT.
Storage:
AR spray roving with standard Zirconia conent 14.5%(ZrO2>14.5%) should be stored in a dry and cool place with their original packaging, the best condition place is being at temperature between 15-35degree and relative humidity between 35%-65%. If AR Spray Roving Pallets are stored at lower temperature (below 15degree), it is advised to condition them in the workshop for 24 hours to prevent condensation.
Application: