CYC Fiberglass Roving for Sheet Molding Compound (SMC Roving)
CYC Fiberglass Assembled Roving for Sheet Molding Compound (SMC Roving) is coated with special silane-based sizing which is compatible with unsaturated polyester resin, vinyl ester resin and epoxy resin. It is desgined for producing automotive parts, doors, chairs, bathtubs, SMC water tanks and sports instruments etc.
| Glass Fiber Type |
E-CR Glass Fiber |
| Filament Diameter |
13 μm |
| Linear Density |
2400, 4800 tex |
Product Characteristics:
Good choppability and good gathering
Good dispersion and lay-down
Low static, excellent mechanical properties
Excellent mold flowability & wet out
Technical Parameters:
|
Linear Density (tex)
|
Filament Diameter (μm)
|
Moisture Content (%)
|
LOI Content (%)
|
|
±5%
|
13±1
|
≤0.1%
|
1.2±0.15%
|
Packaging:
CYC fiberglass roving is packed by standard export pallets.
| Bobbin Height (mm) |
260 |
260 |
| Bobbin Inside Diameter (mm) |
160 |
160 |
| Bobbin Outside Diameter (mm) |
270 |
310 |
| Bobbin Weight (KG) |
16 |
22 |
| Number of Layers |
3 |
4 |
3 |
4 |
| Number of Bobbins per Layer |
16 |
12 |
| Number of Bobbins per Pallet |
48 |
64 |
36 |
48 |
| Net Weight per Pallet (KG) |
768 |
1024 |
792 |
1056 |
Storage:
Unless otherwise specified, CYC fiberglass roving should be stored in a dry, cool and moisture-proof place with its original package, do not open the package before use. The ideal room temperature and humidity should be always maintained at 15℃~35℃ and 35%~65% respectively. To ensure safety and avoid damage to product, the pallet should not stack more than 3 layers high. If the pallets are stacked in 2 or 3 layers, special care should be taken to move top pallet correctly and smoothly.